Anyone Cast Bullets?

Rondo223 · Dec 7, 2023

Join the Cast Boolits forum

Acer-m14 · Dec 8, 2023

Cast Boolits

good place .. i was there years ago ..

learned how to to make black powder 12 ga load back then ..

and make my own bird shot maker ..

they used to have a live chat room ..

Hochulsucks1234 · Dec 8, 2023

I do. Never with wheel weights..just lead bars already hardened (Br.10-15). Use an electric molten pot. I use Lee 2 or 6 cavity molds..aluminum bodied with wood handles. I also use Lee bullet sizing dies after tumbling the bullets in Alox. After that they load nicely.

Lot of things to learn along the way. Never use the first bullets dropped from the molds..or the 2nd..maybe not even third. Drop em back into the melting pot. The molds need to heat up uniformally, or the bullets will have air pockets and be weak. When you do drop bullets, do so in a bucket of water. They will solidify faster. Some don't use the bullet resizers..I swear by them. Each bullet mold has the bullet type on it. Lee has a nice chart on their specs..what type, diameter, sizing die, to lube/not lube, to use/not use gas checks, etc. Cast boolits has the load data that people experiment with.

kev74 · Dec 8, 2023

I cast a bit. Mostly just to know how to do it. Most of what I shoot, I buy.

Watch a bunch of youtube videos, then give it a try. Elvis Ammo has some good info.

Good ventilation and hygiene is a must. Lead poisoning will mess you up - I know from experience from exposure at a previous job. Open a window or do it outside, wash your hands when your done, and especially if you have kids be careful about secondary exposure (clothes, shoes, etc).

Glasses are a good idea. Long pants and long sleeves are a good idea. If you ever had melted solder drip on you, that's what melted lead feels like. A little bit on skin hurts but is bearable, a big spill will mess you up. if it drips on your pants leg, you see it but it doesn't hurt.

Make sure your lead is dry before it goes into a hot pot. Water in melted lead turns to steam and splashes like crazy.

After that, its trial and error. If you mess up, just throw them back in the pot and try again.

When I started, I was tumble-lubing with Alox. Now I use Hi-Tek coating. It works better for me and less messy.

If you have any specific questions, just ask.

fresch · Dec 8, 2023

Get some pure lead and slug the barrel of the guns you will cast for.

fresch · Dec 8, 2023

Perhaps buy the Lyman cast bullet handbook ~*$25
Save tin cans for the slag disposal.
Sawdust, bees wax, Can't think of the chemical added to keep the melt in flux.
Thermometer very important.
Lee smelter/drippers can be fixed with valve grinding powder,
Good set of thick leather (welding) gloves.

Boric acid

Robin · Dec 8, 2023

Just round balls anymore. I used to cast for my centerfire pistols years ago, always used molds that accepted gas checks.
Robin

Hochulsucks1234 · Dec 8, 2023

mgunner said:
Thanks for the information.

I know Rotometals.com sells lead, is that where you buy it? If not, what other sources do you use?

Question about sizing the bullets. Do you size your bullets to SAAMI specs or do you case them .001 or .002 over your bore diameter?

Are you using the bullet sizing die to meet SAAMI specs or are you buying a Lee mold that oversaizes them when cast and then squeezing them down so they are .001 or .002 over you bore diameter?

No problem. So one place I was getting ingots is right from Midway. Cheaperthandirt also.

Lee states that their sizing die should be .001 bigger than the bore. That is a recommendation of course. I load a lot of 45 colt and use the .452 cavity molds. Pushing them through the .452 sizing die really makes a diference imo. Loading straight from the cast I get a lot of lead shaving on the rim of the brass and have to flare the cases to the max. The molds push slightly bigger than .452. Once sized with good lube they load nicely and don't need much pressure. I don't do a lot of loads with gas checks, but gas checks seat much harder into the casing. Gotta be careful crimping, slight crimp is all they can tolerate.

Acer-m14 · Dec 8, 2023

don't forget the snacks when melting lead and casting ..

I think the chips and dust is more hazardous then melting real lead ...

bring the melted lead to a boil then you got issues with lead gasses ..

its the impurities in the lead bar that your melting is what to be safe from ..

that's my opinion ..

i used to use my teeth to pull 22LR bullets from the case when i was a teenager lol

PS .. hell back then they filled your cavity with mercury ..

Acer-m14 · Dec 8, 2023

fresch said:
Get some pure lead and slug the barrel of the guns you will cast for.

mgunner said:
Why should I slug the barrel?

to get the bore diameter

and for your chamber ..

Acer-m14 · Dec 8, 2023

now this lead i would be worried about ..

its called lead oxide .. that dust ..

i have a box of 25 of these to give away ..

any takers ??

LOL ..

fresch · Dec 9, 2023

When you get the book read it.

Lead Thermometer | RCBS

With a 1000°F range and +/- 1 percent accuracy, the RCBS® lead thermometer lets reloaders pour lead at the optimum temperature. Large numbers are printed on a 1 1/2-inch, glass-covered face. Its 6-inch probe works with the RCBS Pro-Melt™ furnace or pot. An adjustable 6-inch handle helps prevent...

www.rcbs.com

If you get the lead too hot the other metals in your mix float to the top in the slag.
It is all in the book.

fresch · Dec 10, 2023

Up next!
Paper patch.

Zerex · Dec 10, 2023

I cast 58 cal miniballs and 12 lead slugs...................
Lead is a danger only in casting and eating lead paint.................kids bite/ teethe on anything..furniture, cribs rails, toys......woodwork...........

At some point keeping several hundred lbs of lead around you home in cast bullets or ingots will convict you for a death penalty, as a racist..........Cal did..........

repete · Dec 10, 2023

I still do some, I have a lot already cast up in various calibers so only cast about one or two days a year. I use mostly wheel weights followed by berm turds and finally new alloy's from Roto Metals. I use super hard from Roto Metals to harden up the berm turds, I used to have a Lee hardness tester until I loaned it out. Oh well, back to the xx pounds of WW and so much solder to make such n such, I shoot mostly Lyman#2 like recipes and size with a Lyman sizer/luber and install gas checks if needed. I do have some Lee sizers and use them, Alox not so much. Seems to be to damn messy and sticky! It does work great for .38 wadcutters! After loading I just wipe the face of the bullet with a rag and solvent, no more sticky mess.
I don't EVER get anything from cheaper than dirt! In my opinion they're back stabbing POS!
Midway is a bit pricey and shipping adds up.
I use a mix of differing molds from differ makers, some aluminum, steel, brass. The very best ones I have are NOE brass , once you use one of his molds you really won't want to go back to the LEE aluminum again! But $$ is a big factor starting out.
As for lead. Ask around wheel weights are real hard to come by now, but they are still out there. Battery terminals and clamps can be a source DO NOT USE BATTERY PLATES THEMSELVES!! Bad juju.
I used to always carry an empty cup going down range to change targets, while guys are walking back from the 100 yd line, I'd fill the cup with range turds at the 25yd line, free lead for just picking it up. DO NOT DIG UP THE BERMS!
Last year I gave 8 very full 5 gallon buckets of lead away ( to the same guy who borrowed my lead tester), sometimes you just realize you have to much.

fresch · Dec 10, 2023

I did a job at the local stage and was given 3 65lbs weights that balance the lighting and curtains. Big old hunks of lead, use my hammer drill with the chisel bit to cut them up.
Down to 1 5gal bucket of WW, shoot Lyman #2 (or close to it).
Then I got lazy and bought a couple of pre made .38, .45, back when things were cheaper ~ obama era.

Xae289 · Dec 10, 2023

I don't cast myself but have tried many cast bullets. I got a batch of Hi Teks that leaded the barrel of one of my revolvers horribly. I figured out they were too big and guessed that the coating was coming off as each bullet squeezed through the cylinder. I pan lubed the batch and that totally eliminated the leading.

Tumble lubing is easy, but pan lubing can give great results. I did it with a mix of generic petroleum jelly and bees' wax. I forget the ratio since I only mixed up one big jarful and still have some left, but it's out there somewhere. If tumble lubing doesn't work out great for you, pan lubing is a relatively easy backup plan to keep in the back pocket.

Acer-m14 · Dec 11, 2023

mgunner said:
I asked one of the guys at my garage if they could ask the owner about wheel weights. I have to call them back to see what they say.

its been i would say like 5 yrs now since i hit the car dealer here up for 5 gal pails of wheel weights ..

got 4 pails and there all a mix of lead and FE ( steel ) and Zinc weights ..

you might get 5 or 10 lbs out them these days if your lucky .. or nothing at all ..

i still have 2 pails to sort through from 5 yrs ago .. i'll most likely get 15 to 25 lbs from each pail ..

i would not pay anything for a pail of wheel weights these days .. just gladly to take them off your hands ..

PS .. un less I'm seeing actual lead weighs on the top layer of the pail ..

Acer-m14 · Dec 11, 2023

mgunner said:
Good advice thank you. I saw a video about about zinc and steel wheel weights and how to tell them apart.

just hold a like a 9/16th wrench in your hand ..

wack a few steel and zinc and some lead .. you will know the sound of lead ..

a dull thump .. no ring ..

or just a knife .. it will slice and dig in on the lead weight with little effort .. will not do shit to the steel and zinc

Anyone Cast Bullets?

.45 acp

.950 JDJ

.357 mag

.45 acp

20×102mm Vulcan

.44 mag

20×102mm Vulcan

.338 Win Mag

.338 Win Mag

.577 Tyrannosaur.

.45 acp

.45 acp

.45 acp

.44 mag

20×102mm Vulcan

20×102mm Vulcan

20×102mm Vulcan

.338 Win Mag

.338 Win Mag

.308 Win

.338 Win Mag

.338 Win Mag

.45 acp

.223 Rem

.45 acp

.45 acp

.45 acp

20×102mm Vulcan

.45 acp

20×102mm Vulcan